PHYSICAL PROPERTY TEST DATA
Material : N7001 Color :BLACK Date :20070201
Press Cure Sheet: 6 min 170 ℃ Button: 30 min 160 ℃ O-ring: S ℃
Post Cure Sheet: min ℃ Button: min ℃ O-ring: S ℃
Customer TEL:0592-6313227 FAX:0592-6313223
SPECIFICATION: ASTMD2000 M2BG714A14B14EA14EF11EF21EO14EO34F17 |
* ITEM |
REQUIRED |
TEST DATA |
* Original Property |
Hardness, Pts SHOREA |
70+/-5 |
72 |
Specific Gravity , g/cm3 |
|
1.24 |
Modulus , % |
|
|
Tensile strength |
14Mpa |
15.4Mpa |
Elongation, % |
250 |
380 |
* A14 Heat Aged , ASTM D 573 70 Hrs at 100 ℃ |
Hardness Change , Pts |
+/-15 |
+3 |
Tensile Strength Change , % |
+/-30 |
+5.1 |
Elongation Change , % |
-50 |
-26.7 |
* B14 Compression Set , ASTM D395 Method B 22 Hrs at 100 ℃ |
Deflection , % ( button) |
25 |
7.5 |
*Z O-ring Compression Set, ASTM D1414 _______Hrs at _____ ℃ |
Deflection , % |
|
|
C Ozone Resistance, pphm h at ℃ |
|
|
*EA14 Water Resistance , ASTM D471 70 Hrs at 100 ℃ |
Hardness Change , Pts |
+/-10 |
-3.6 |
Tensile Strength Change , % |
|
|
Elongation Change , % |
|
|
Volume Change , % |
+/-15 |
+9.5 |
*EF 11 Fluid Resistance, Ref. Fuel A , ASTM D471 70 Hrs at 23 ℃ |
Hardness Change , Pts |
+/-10 |
-3 |
Tensile Strength Change , % |
-25 |
-8 |
Elongation Change , % |
-25 |
-13.4 |
Volume Change , % |
-5~+10 |
+2.2 |
*EF 21 Fluid Resistance, Ref. Fuel B , ASTM D471 70 Hrs at 23 ℃ |
Hardness Change , Pts |
-30~0 |
-12 |
Tensile Strength Change , % |
-60 |
-29.1 |
Elongation Change , % |
-60 |
-25.6 |
Volume Change , % |
0~+40 |
+21.9 |
*EO14 Fluid Resistance, ASTM # 1 oil , ASTM D471 70 Hrs at 100 ℃ |
Hardness Change , Pts |
-5~+10 |
+5 |
Tensile Strength Change , % |
-25 |
+7.4 |
Elongation Change , % |
-45 |
-28.7 |
Volume Change , % |
-10~+5 |
-6.4 |
*EO34 Fluid Resistance, ASTM # 3 oil , ASTM D471 70 Hrs at 100 ℃ |
Hardness Change , Pts |
-10~+5 |
-5 |
Tensile Strength Change , % |
-45 |
+3.8 |
Elongation Change , % |
-45 |
-22.6 |
Volume Change , % |
0~+25 |
+7.6 |
*F17 Low-temperature nonbrittle after 3min at -40℃ |
|
PASS |
|
|
|
|
|
Engineer:_____ Plant Manager: ______
XIAMEN HAIYIXIN RUBBER SEAL CO.,LTD
PHYSICAL PROPERTY TEST DATA
Material :E7001 Color : BLACK Date : 20070201
Press Cure Sheet: 12 min 170℃ Button: 30 min 160 ℃ O-RING: S ℃
Post Cure Sheet: min ℃ Button: min ℃ O-RING: min ℃
Customer: TEL:0592-6313227 FAX:0592-6313223
SPECIFICATION: M2BA710A14B13EA14F17 (Z1=70±5 ) |
* ITEM |
REQUIRED |
TEST DATA |
* Original Property |
Hardness, shore A, Pts |
70±5 |
73 |
Specific Gravity , g/cm3 |
|
|
Modulus, %,psi |
|
|
Tensile strength , N/mm2 |
10 |
14.7 |
Elongation, % |
300 |
328 |
* A 14 Heat Aged , ASTM D 573 70 Hrs at 100℃ |
Hardness Change , Pts |
±15 |
+1 |
Tensile Strength Change , % |
±30 |
-8.2 |
Elongation Change , % |
-50 |
-31.3 |
* B 13 Compression Set , ASTM D395 Method B 22Hrs at 70℃ |
Deflection , % |
50 |
13 |
*C Ozone Resistance, _____pphm ____h at ____ ℃ |
|
|
*EA14 Water Resistance , ASTM D471 70 Hrs at100 ℃ |
Hardness Change , Pts |
|
-1 |
Volume Change , % |
10 |
+0.7 |
Elongation Change , % |
|
|
Tensile Strength Change , % |
|
|
*EF Fluid Resistance, Ref. Fuel A , ASTM D471 Hrs at ℃ |
Hardness Change , Pts |
|
|
Tensile Strength Change , % |
|
|
Elongation Change , % |
|
|
Volume Change , % |
|
|
*EF Fluid Resistance, Ref. Fuel B , ASTM D471 Hrs at ℃ |
Hardness Change , Pts |
|
|
Tensile Strength Change , % |
|
|
Elongation Change , % |
|
|
Volume Change , % |
|
|
*EO Fluid Resistance, ASTM # 1 oil , ASTM D471 Hrs at ℃ |
Hardness Change , Pts |
|
|
Tensile Strength Change , % |
|
|
Elongation Change , % |
|
|
Volume Change , % |
|
|
*EO Fluid Resistance, ASTM # 3 oil , ASTM D471 Hrs at ℃ |
Hardness Change , Pts |
|
|
Tensile Strength Change , % |
|
|
Elongation Change , % |
|
|
Volume Change , % |
|
|
*F17 Low-temperature nonbrittle after 3_min at -40℃ |
PASS |
PASS |
Engineer: Plant Manager: ____
XIAMEN HAIYIXIN RUBBER SEAL CO;LTD
PHYSICAL PROPERTY TEST DATA
Material : SIL5001 Color : BRU Date : 20070201
Press Cure Sheet: 12 min 170℃ Button: 30 min 160 ℃ O-RING: S ℃
Post Cure Sheet: 240 min 200℃ Button: 240 min 200 ℃ O-RING: min ℃
Customer: TEL:0592-6313227 FAX:0592-6313223
SPECIFICATION:ASTM D2000 5GE508A19B37EO36C12F19G11 |
* ITEM |
REQUIRED |
TEST DATA |
* Original Property |
Hardness, shore-A, Pts |
50+/-5 |
50 |
Specific Gravity , g/cm3 |
|
1.15 |
Modulus, %,psi |
|
213 |
Tensile strength , min, psi |
800 |
1198 |
Elongation,min ,% |
250 |
420 |
* A 19 Heat Aged , ASTM D 573 70 Hrs at 225 ℃ |
Hardness Change , Pts |
+10 |
+1 |
Tensile Strength Change , max, % |
-25 |
-15.2 |
Elongation Change , max,% |
-30 |
+8.2 |
* B 37 Compression Set , ASTM D395 Method B 22 Hrs at 175℃ |
Deflection , % |
25 |
15.8 |
*C 12 Ozone Resistance, 50 pphm 72 h at 40 ℃ |
|
NO crack |
*EA Water Resistance , ASTM D471 Hrs at ℃ |
Hardness Change , Pts |
|
|
Volume Change , % |
|
|
Elongation Change , % |
|
|
Tensile Strength Change , % |
|
|
*EF Fluid Resistance, Ref. Fuel C, ASTM D471 Hrs at ℃ |
Hardness Change , Pts |
|
|
Tensile Strength Change , % |
|
|
Elongation Change , % |
|
|
Volume Change , % |
|
|
*EF Fluid Resistance, Ref. Fuel B , ASTM D471 Hrs at ℃ |
Hardness Change , Pts |
|
|
Tensile Strength Change , % |
|
|
Elongation Change , % |
|
|
Volume Change , % |
|
|
*EO Fluid Resistance, ASTM # 1 oil , ASTM D471 Hrs at ℃ |
Hardness Change , Pts |
|
|
Tensile Strength Change , % |
|
|
Elongation Change , max,% |
|
|
Volume Change , max, % |
|
|
*EO 36 Fluid Resistance, ASTM # 3 oil , ASTM D471 70 Hrs at 150℃ |
Hardness Change , Pts |
-30 |
-19.8 |
Tensile Strength Change , % |
|
|
Elongation Change , % |
|
|
Volume Change , % |
+60 |
+53.4 |
*F19Low-temperature nonbrittle after 3min at –55℃ |
|
pass |
*G 11 Tear resistance ASTM D624 DieB |
|
18.3KN/m |
Engineer: Plant Manager: _____
XIAMEN HAIYIXIN RUBBER SEAL CO;LTD
PHYSICAL PROPERTY TEST DATA
Material : V7001 Color : BLACK Date : 20070201
Press Cure Sheet: 12 min 170℃ Button: 30 min 160 ℃ O-RING: S ℃
Post Cure Sheet: 1440 min 230℃ Button: 1440min 230 ℃ O-RING: min ℃
Customer: TEL:0592-6313227 FAX:0592-6313223
SPECIFICATION:ASTM D2000 M2HK810A1-10B38EF31EO78F15 |
* ITEM |
REQUIRED |
TEST DATA |
* Original Property |
Hardness, Shore-A, Pts |
70+/-5 |
73 |
Specific Gravity , g/cm3 |
|
1.86 |
Modulus, 100 %,Mpa |
|
7.3 |
Tensile strength , min, MPa |
10 |
14.5 |
Elongation,min ,% |
150 |
215 |
* A1-10 Heat Aged , ASTM D 573 70 Hrs at 250℃ |
Hardness Change , Pts |
+10 |
+3 |
Tensile Strength Change , max, % |
-25 |
-6.0 |
Elongation Change , max,% |
-25 |
-2.6 |
* B 38 Compression Set , ASTM D395 Method B 22 Hrs at 200℃ |
Deflection , % |
50 |
22.3 |
*C Ozone Resistance, _____pphm ____h at ____ ℃ |
|
|
*EA Water Resistance , ASTM D471 Hrs at ℃ |
Hardness Change , Pts |
|
|
Volume Change , % |
|
|
Elongation Change , % |
|
|
Tensile Strength Change , % |
|
|
*EF 31 Fluid Resistance, Ref. Fuel C, ASTM D471 70 Hrs at 23 ℃ |
Hardness Change , Pts |
+/-5 |
+1 |
Tensile Strength Change , % |
-25 |
-8.2 |
Elongation Change , % |
-20 |
+2.7 |
Volume Change , % |
0~+10 |
+2.0 |
*EF Fluid Resistance, Ref. Fuel B , ASTM D471 Hrs at ℃ |
Hardness Change , Pts |
|
|
Tensile Strength Change , % |
|
|
Elongation Change , % |
|
|
Volume Change , % |
|
|
*EO 78 Fluid Resistance, ASTM # 1 oil , ASTM D471 70 Hrs at 200℃ |
Hardness Change , Pts |
-15~+5 |
-2 |
Tensile Strength Change , % |
-40 |
-7.7 |
Elongation Change , max,% |
-20 |
+5.3 |
Volume Change , max, % |
0~+15 |
+10.2 |
*EO Fluid Resistance, ASTM # 3 oil , ASTM D471 Hrs at ℃ |
Hardness Change , Pts |
|
|
Tensile Strength Change , % |
|
|
Elongation Change , % |
|
|
Volume Change , % |
|
|
*F15 Low-temperature nonbrittle after 3min at -25℃ |
PASS |
PASS |
Engineer: Plant Manager: _____
|